Marble Adhesive
AoLiBao Marble Adhesive
2017-02-23 10:08:33    Source:    Browse:614次

 

Marble Adhesive

BrandAoLiBao

Details

Main Ingredients

Unsaturated Polyester ResinPeroxides fillers

Main purpose                                                       
Widely used in building stone , ceramics , high-grade stone processing , tiles quickly locate and parquet , repair  and  bonding.

Features:  

1. Ultra- resistant solid                                                                 
Super earthquake resistance , tensile strength, impact resistance . It can pull of stone when bonding stone without intact the glued joints.
With strong resilience and scalability , prevent adhesion due to a strong external force deformed , distorted , shedding .

2.  Ultra- temperature resistant                                                    
Ensure the normal use of the products under -10
 to 45 ° C temperature difference. Breakthrough restricted ordinary stone bonding glue in low temperature in winter. Suitable for contruction in poor condition in winter , northern , low temperature (-10 ) .

Intensity of technical parameters

No.

 Project Name

Detection conditions

Technical target

 1

 Shear bonding strength

 Standard maintenance 48h

16.52MPa

 2

 Shear bonding strength

 Standard maintenance 168h

15.94MPa

 3

 Shear bonding strength

 After maintenace 168hthen 100/168h

10.50MPa

 4

vertical tensile bond strength

 Standard maintenance 168h

8.56MPa

The physical characteristics

A component

 Resin category

 Unsaturated Polyester Resin

 Morpha

Transparent paste

yellow transparent liquid

Colored paste

Colored semifluid

 Density

1.05-1.15g/ cm3

1.05-1.15g/ cm3

1.5-1.7/ cm3

1.4-1.6g/ cm3

 Viscocity

100,000-300,000c.p

700-900c.p

350,000-800,000c.p

4.000-8.000c.p

 Hazardous Decomposition

 It will realse carbon monoxide and carbon dioxide in fire

 Disposal

 Disposal or processing as formal procedures in Country or region

 B component

 Main ingredient

 Organic peroxides

 Morpha

 White paste gel

 Density

 1.12-1.18g/ cm3

 Viscocity25

 100,000-200,000c.p

 Storage period10-25

 12 months in original packaging

 Hazardous Decomposition

 It will react in fire and release carbon dioxide

 Disposal

 Disposal or processing as formal procedures in Country or region

Usage

1Bonding surface should be clean and dry with slightly rough texture.

2Taken 100 parts glue mix 3 parts hardener, and mix well, then applied to the treated surface with gel tools  

Technical target

  No.

 Items

Q/WKD002-2002

 1

Shear strength stone-stone

 Standard

≥8Mpa

 80168 hours heating treatment

≥7Mpa

 25168 hours water intrusion

≥5Mpa

 25 times freeze-thaw cycles

≥4Mpa

 VOC contents

≤350g/L

 2

Limit of harmful substances

 benzene

≤1g/kg

 Toluene + xylene

≤50g/kg

 Formaldehyde

≤0.1g/kg

Solidify time

temperaturec

Working time

Gel time

Complete solidify time

 0-10

8

10

12

 10-20

5

7

8

 20-30

3

5

6

 30-40

2

3

4


 Attention

1 Don't put mixed glue back into the tank

2 If you need to speed up or slow down the solidify time,pls add more or reduce the hardener.

3 Adhesive surface should be clean and dry,otherwise it will lead to bonding loose.

4 Please store in cool, dark place,and lid be closed stick after used every time.

5 Working environmental temperature should be less than 50

6 Do not expose to the moist and frosty environment frequently.

7 If to be bonding the hanging parts, please choose our epoxy AB Adhesive

 Packaging

   Packing  capacity:
      
  

Capacity Weight Packing CTNS PACKAGE WEIGHT
1 L 1kg tin 12 tins 12 kgs
4 L 4kg tin 4 tins 16 kgs
18 L 18kg pail none 18 kgs

     


                     

Last oneNo
Next articleNo
Headquarters address:China Fuzhou Fujian District Economic and Technological Development Zone Economic and Technological Development Zone No. 190
Tel:400-0133-656 fax:0591-83657007
Copyright © 2016 Fuzhou aolibao Building Materials Technology Co., Ltd. copyright
Technical support:19 network